The failure of the roll during rolling process causes cobble to lose production time for several hours. Investigations include visual inspection, lltrasonic test, chemical analysis, metallography, and hardness measurement. Stand finishing F1-F4 uses High Chrome (HCr) material type, while F5-F6 ICDP type. Spalling work occurs on stand F5 with Roll Top position. was chipped between shell core an ...

Porosity is a major concern in the production of light metal parts. This work aims to identify some of the mechanisms of microporosity formation during the gravity-poured castings of magnesium alloy AE42. Two graphite plate molds and a ceramic cylindrical mold were selected to produce a wide range of cooling rates. Temperature data during cooling was acquired with type K thermocouples at 60 Hz ...

Ferrite of austeno-ferritic stainless steels maintained for a long time at temperatures in the range of 270 °C to 400 °C is embrittled like the known 475 °C embrittlement of ferritic stainless steels. Deformation and damage micromechanisms of a material must be known in order to apply the “local approach to fracture” (LAF) methodology. In this work we test a previous model of damage nucleation ...

  Friction-stir welding process is a novel method of solid state welding, which produces heat due to friction between the pin, the shoulder and the workpiece. This heat causes a paste area. Shoulder pressure and pin spin cause edges integration and lead to welding. In this study, firstly, the feasibility of welding of steel sheet (EN10130) with a thickness of 1.5mm has been tested by 58 experim...