In this work, the effects of carbon content and manganese sulfide addition on the microstructure and mechanical properties of copper steel parts have been studied. Steel powder mixture containing 2%Cu and different graphite contents with and without MnS additions were compacted, sintered and forged to almost full density. Forged samples, with near theoretical densities, were tested for tensile,...

In this paper, failure mechanism of a 17th stage blade of an 82.5 MW steam turbine that caused damage to the internal turbine compartment and the adjacent blade equipment has been studied. In order to determine the cause of failure and prevent similar events, various metallurgical and mechanical investigations including chemical composition analysis, metallography and microstructural analysis, ...

In this paper, failure mechanism of a 17th stage blade of an 82.5 MW steam turbine that caused damage to the internal turbine compartment and the adjacent blade equipment has been studied. In order to determine the cause of failure and prevent similar events, various metallurgical and mechanical investigations including chemical composition analysis, metallography and microstructural analysis, ...

In this and the subsequent companion paper, results are presented that collectively seek to delineate the contribution that supraspinal circuits have in determining the time to task failure (TTF) of sustained submaximal contractions. The purpose of this study was to compare adjustments in supraspinal and spinal excitability taken concurrently throughout the performance of two different fatigue ...

Orthopaedic implants experience large cyclic loads, and pre-clinical analysis is conducted to ensure they can withstand millions of loading cycles. Acetabular cup developments aim to reduce wall thickness to conserve bone, and this produces high pre-stress in modular implants. As part of an implant development process, we propose a technique for preclinical fatigue strength assessment of modula...

The biaxial flexural strength and cyclic fatigue biaxial flexural strength of CAD/CAM ceramics polished with #220, 400, 600 and 1000 diamond pads were measured in an effort to determine the effect of surface roughness on fatigue behavior of dental ceramics. The surface roughness was improved after polishing with a smaller diamond grain pad. The flexural strengths of the specimens polished with ...

Fatigue behaviors of structural adhesives composed of epoxide resin and aliphatic α, ω-dicarboxylic acids HOOC-(CH2)p-COOH (p=2, 4, 8 or 10) were investigated by analyzing the results of fatigue test and bulk properties of the systems. The fatigue strength and maximum value of damping increased with increasing p. The glass transition temperature, tensile strength, shear adhesive strength by ten...