The fracture and crack growth of mechanical structures is a usual phenomenon which is due to the application of tensile, cyclic loading or thermal stresses on the structure. So introducing of methods to prevent the crack growth is useful. Afterward, one of the repairing methods of crack growth, consisting to make a hole in the crack tip to elimi-nate the sharp corners, was explained. This metho...

Compressive failure by splitting is studied herein via an analytical model. The use of a shear lag model to determine the stress state at the crack tip and the modeling of the region away from the crack tip by the 3D elasticity equations leads to a simple analytical expression is used to determine the compliance changes for both unsteady crack growth as well as steady state crack growth under c...

In the aerospace and aviation sectors, the damage tolerance concept has been applied widely so that the modeling analysis of fatigue crack growth has become more and more significant. Since the process of crack propagation is highly nonlinear and determined by many factors, such as applied stress, plastic zone in the crack tip, length of the crack, etc., it is difficult to build up a general an...

in this paper, three-dimensional modeling of the fatigue crack growth profiles was performed in a simple riveted lap joint. simulation results showed that mode i was dominated on the one side of the plates and the crack straightly grew on this side, while the other side of the plates was in a mixed-mode condition and the crack propagation path was not straight on this side. afterward, the fract...

This paper focuses on the analysis of the partial differential equations arising from a new approach to modeling brittle fracture based on an extension of continuum mechanics to the nanoscale. It is shown that ascribing constant surface tension to the fracture surfaces and using the appropriate crack surface boundary condition given by the jump momentum balance, leads to a sharp crack opening p...

The growth of slant cracks by fretting fatigue of a half plane in contact with a flat rounded pad was studied. The mode I and mode II stress intensity factors for cracks of various lengths and directions were calculated using the semi-analytical method of the distribution of dislocations, and their cumulative effect on the crack growth was investigated using the strain energy density criterion....

Study about Fracture Mechanics and the root cause of fracture in order to estimates lifetime for Mechanical parts in designing process and manufacturing have tremendous role in this realm. Stress intensity factor comes into design which not only is dependent to geometry also extremely to load condition; for instance, it is important in failure processes (brittle and ductile Materials) or to pre...