A finite-element procedure is developed to analyze plane ductile fracture problems in the presence of largescale yielding near the crack tip. Strain and stress singularities near the crack tip, corresponding to the strainhardening material model, are embedded in elements near the crack tip. The developed elastic-plastic incremental finite-element method is based on a hybrid displacement model. ...

This paper presents a low cycle fatigue life curve by simulating a crack in a cover plate welded moment connection. Initiation of ductile fracture in steel is controlled by growth and coalescence of micro-voids. This research used a numerical method using finite element modeling and simulation of ductile crack initiation by a micromechanical model. Therefore, a finite element model of a cover p...

In sheet metal forming processes with complex strain paths, a part is subjected to large plastic deformation. This severe plastic deformation leads to high plastic strain localization zones and subsequent accumulation of those strains. Then internal and superficial micro-defects and in other words ductile damage is created. This damage causes quality problems such as fracture. Therefore, design...

Stable ductile crack growth in 3 mm thick AISI 304 stainless steel specimens has been investigated experimentally and numerically. Multi-linear Isotropic Hardening method coupled with the Von-Mises yield criterion was adopted for modeling elasto-plastic behavior of the material. Mode-I CT fracture specimens have been tested to generate experimental load-displacement-crack growth data during sta...

In this work, a meshfree method is used to simulate thermo-mechanical ductile fracture under finite deformation. A Galerkin meshfree formulation incorporating the Johnson-Cook damage model is implemented in numerical computations. We are interested in the simulation of thermomechanical effects on ductile fracture under large scale yielding. A rate form adiabatic split is proposed in the constit...

Modeling of crack propagation by a finite element method under mixed mode conditions is of prime importance in the fracture mechanics. This article describes an application of finite element method to the analysis of mixed mode crack growth in linear elastic fracture mechanics. Crack - growth process is simulated by an incremental crack-extension analysis based on the maximum principal stress c...

Ductile fracture modeling still has to be improved at the macro and microscales. New numerical methods are applied to the limit analysis of cells containing one or several voids or void clusters. The results are compared with existing macroscopic models. Voids can also be introduced in analytical polycrystalline models, in order to combine plastic anisotropy and texture evolution with ductile f...

Ductile-brittle fracture transition was investigated using compact tension (CT) specimens from -70 o C to 40 o C for a carbon steel. Large deformation finite element analysis has been carried out to simulate the stable crack growth in the compact tension (CT, a/W=0.6), three point-point bend (SE(B), a/W=0.1) and centre-cracked tension (M(T), a/W=0.5) specimens. Experimental crack tip opening di...

An elastic finite element analysis was conducted to evaluate the stress distribution in the initiation zone of the adhesive rupture during the 3-point bending test. This test is used to measure the adherence between a polyepoxy adhesive and aluminum alloy with different surface treatments. The purpose is to compare, in the high stress concentration areas, the stress fields calculated using fini...